Volume 38 Issue 4
Jul.  2020
Turn off MathJax
Article Contents

ZHANG Lingna, WANG Tianyu, HONG Wanfeng, TAO Chun, SONG Hongtao. Preparation and formulation optimization of wound dressings with nitrocellu-lose as membrane material[J]. Journal of Pharmaceutical Practice and Service, 2020, 38(4): 301-306. doi: 10.12206/j.issn.1006-0111.201910082
Citation: ZHANG Lingna, WANG Tianyu, HONG Wanfeng, TAO Chun, SONG Hongtao. Preparation and formulation optimization of wound dressings with nitrocellu-lose as membrane material[J]. Journal of Pharmaceutical Practice and Service, 2020, 38(4): 301-306. doi: 10.12206/j.issn.1006-0111.201910082

Preparation and formulation optimization of wound dressings with nitrocellu-lose as membrane material

doi: 10.12206/j.issn.1006-0111.201910082
  • Received Date: 2019-10-25
  • Rev Recd Date: 2020-03-16
  • Available Online: 2020-07-27
  • Publish Date: 2020-07-25
  •   Objective  To prepare a wound dressing using nitrocellulose as a membrane and optimize its formulation.  Methods  Partial analysis was performed on commercial available products. The wound dressings were prepared by using nitrocellulose as a film-forming material, benzyl alcohol as a bacteriostatic agent, castor oil as a plasticizer, isopropyl palmitate as a skin emollient, camphor as a fragrance, and isopropyl alcohol, ethyl acetate and butyl acetate as volatile solvent. The tensile strength, breakpoint elongation percentage, breathability and waterproof performance were tested and evaluated.  Results  The film-forming performance of the prepared liquid wound dressing was good. The final use amount of nitrocellulose was determined to be 6%. The use amount of plasticizer castor oil was determined to be 4%.  Conclusion  The prepared liquid wound dressing has good film-forming property, good mechanical property, good waterproof and certain breathability.
  • [1] WINTER G D. Formation of the scab and the rate of epithelisation of superficial wounds in the skin of the young domestic pig. 1962[J]. J Wound Care,1995,4(8):366-371. doi:  10.12968/jowc.1995.4.8.366
    [2] EAGLSTEIN W H, SULLIVAN T P, GIORDANO P A, et al. A liquid adhesive bandage for the treatment of minor cuts and abrasions[J]. Dermatol Surg,2002,28(3):263-267.
    [3] CASPER K A. OTC product: band-aid liquid bandage[J]. J Am Pharm Assoc,2006,46(6):768. doi:  10.1331/1544-3191.46.6.768.Casper
    [4] GREIG, LY NN. First aid for minor burns, cuts and grazes[J]. Australian Pharmacist,2012,31(6):464-465.
    [5] ZHANG D, ZHOU W, WEI B, et al. Carboxyl-modified poly(vinyl alcohol)-crosslinked chitosan hydrogel films for potential wound dressing[J]. Carbohydr Polym,2015,125:189-199. doi:  10.1016/j.carbpol.2015.02.034
    [6] SIRITIENTONG T, RATANAVARAPORN J, SRICHANA T, et al. Preliminary characterization of genipin-cross-linked silk sericin/poly(vinyl alcohol) films as two-dimensional wound dressings for the healing of superficial wounds[J]. Biomed Res Int,2013,19(6):235-246.
    [7] ROBINS P, GOLDBERG L, MOY R, et al. The effectiveness of liquid bandage as an adhesive and antimicrobial agent[J]. J Drugs Dermatol,2008,7(8):764-766.
    [8] WOO K Y, CHAKRAVARTHY D. A laboratory comparison between two liquid skin barrier products[J]. Int Wound J,2014,11(5):561-566. doi:  10.1111/iwj.12325
    [9] DU L N, TONG L, JIN Y G, et al. A multifunctional in situ-forming hydrogel for wound healing[J]. Wound Repair Regen,2012,20(6):904-910. doi:  10.1111/j.1524-475X.2012.00848.x
    [10] HUANG Y C, CHU H W, HUANG C C, et al. Alkali-treated konjac glucomannan film as a novel wound dressing[J]. Carbohydr Polym,2015,117:778-787. doi:  10.1016/j.carbpol.2014.10.047
  • 加载中
通讯作者: 陈斌, bchen63@163.com
  • 1. 

    沈阳化工大学材料科学与工程学院 沈阳 110142

  1. 本站搜索
  2. 百度学术搜索
  3. 万方数据库搜索
  4. CNKI搜索

Figures(14)

Article Metrics

Article views(5253) PDF downloads(46) Cited by()

Related
Proportional views

Preparation and formulation optimization of wound dressings with nitrocellu-lose as membrane material

doi: 10.12206/j.issn.1006-0111.201910082

Abstract:   Objective  To prepare a wound dressing using nitrocellulose as a membrane and optimize its formulation.  Methods  Partial analysis was performed on commercial available products. The wound dressings were prepared by using nitrocellulose as a film-forming material, benzyl alcohol as a bacteriostatic agent, castor oil as a plasticizer, isopropyl palmitate as a skin emollient, camphor as a fragrance, and isopropyl alcohol, ethyl acetate and butyl acetate as volatile solvent. The tensile strength, breakpoint elongation percentage, breathability and waterproof performance were tested and evaluated.  Results  The film-forming performance of the prepared liquid wound dressing was good. The final use amount of nitrocellulose was determined to be 6%. The use amount of plasticizer castor oil was determined to be 4%.  Conclusion  The prepared liquid wound dressing has good film-forming property, good mechanical property, good waterproof and certain breathability.

ZHANG Lingna, WANG Tianyu, HONG Wanfeng, TAO Chun, SONG Hongtao. Preparation and formulation optimization of wound dressings with nitrocellu-lose as membrane material[J]. Journal of Pharmaceutical Practice and Service, 2020, 38(4): 301-306. doi: 10.12206/j.issn.1006-0111.201910082
Citation: ZHANG Lingna, WANG Tianyu, HONG Wanfeng, TAO Chun, SONG Hongtao. Preparation and formulation optimization of wound dressings with nitrocellu-lose as membrane material[J]. Journal of Pharmaceutical Practice and Service, 2020, 38(4): 301-306. doi: 10.12206/j.issn.1006-0111.201910082
  • 皮肤是人体最大的器官,日常生活中难免受到损伤形成伤口,如轻微的皮肤擦伤、割伤和烧伤等。对于日常的小伤口,一般可以任其自愈,但若稍不注意沾水或接触外界细菌,则容易造成感染,影响伤口愈合,甚至造成溃烂。我们常用的创面处理方法有:使用创可贴覆盖;双氧水或碘伏消毒处理;纱布包扎等。这些处理方法存在着防水透气性差、撕除时疼痛和使用不便等问题。20世纪60年代,Winter博士的研究证实了湿润的伤口环境有助于上皮组织更快的形成,并以此为依据提出了“湿性愈合”的概念[1]。这一研究提高了人们对伤口护理的认识,也为研发封闭敷料奠定了基础。由于传统的敷料不能在伤口处使用较长时间,也不能为伤口愈合提供一个湿润的环境,因此,各种高科技的湿性疗法的伤口护理产品层出不穷。在日本及美国等发达国家,出现以硝化纤维为主要材料的新型创伤敷料[2-4],可用于密封小型伤口甚至保护烧伤创面。此类创伤敷料在使用前为液体形态,涂抹在伤口后有机溶剂迅速挥发,短时间覆盖伤口形成保护膜,具有防水、杀菌、预防伤口感染等优点[5-7]。本研究拟以市售小林液体创可贴为基础,以硝化纤维为膜材,优化处方,制备一种性能更为优良的液体创伤敷料。

  • Agilent 1200高效液相色谱仪(美国Agilent公司);Shimadzu HS-20气相色谱仪(日本Shimadzu公司);拉力试验机(上海和晟仪器有限公司);AL204型电子天平(上海梅特勒-托利多仪器有限公司);D2400型纯水/超纯水一体机(美国明澈公司);25型无极调速电动搅拌机(江苏江阴科技器械厂)。

  • 小林液体创可贴(日本小林制药株式会社);硝化纤维(衡水东方化工有限公司);蓖麻油、樟脑、苯甲醇、乙酸丁酯、异丙醇、N,N-二甲基甲酰胺、甲醇(均为国药集团化学试剂有限公司);棕榈酸异丙酯(IPP,青岛优索化学科技有限公司);乙酸乙酯(上海联试试剂有限公司)。

  • 采用高效液相色谱法测定,色谱条件:采用Agilent 1200高效液相色谱仪;色谱柱:ODS-C18色谱柱;流动相:甲醇-水(50∶50 V/V);流速:1.0 ml/min;进样量:20 μl;柱温:40 ℃;检测波长:257 nm。

    标准曲线的绘制:精密称定苯甲醇对照品151.3 mg置于100 ml容量瓶中,用甲醇稀释至刻度;精密量取上述溶液1、2、2.5、3、4 ml于25 ml容量瓶中,用甲醇稀释至刻度。市售产品(供试品)溶液的配制:精密称定244.3 mg市售产品于50 ml容量瓶中,用甲醇稀释至刻度。

    实验结果:色谱图良好,苯甲醇对照品及市售产品均在5.87 min附近有峰且峰型良好。标准曲线回归方程为:Y = 13040X + 212.7 (r=0.999);经计算得市售产品苯甲醇的使用量为4.0%。

  • 采用气相色谱法测定,色谱条件:采用 HS-20气相色谱仪;色谱柱:DB-624毛细管柱;载气:H2 50 ml/min;空气450 ml/min;进样量:1 μl;柱温:40 ℃/min持续3 min,10 ℃程序升温至200 ℃,持续1 min;检测器温度:250 ℃;气化室温度:220 ℃;FID检测器。

    标准曲线的绘制:精密称定异丙醇1.0077 g,乙酸乙酯0.9933 g,乙酸丁酯1.0014 g于100 ml容量瓶中,加入适量N,N-二甲基甲酰胺(DMF)混合均匀,用DMF稀释至刻度。分别取上述溶液0.1、0.25、0.5、0.75、1.0 ml置于25 ml容量瓶中,用DMF稀释至刻度。

    市售产品(供试品)溶液的配制:精密称定1.186 0 g市售产品于100 ml容量品中,加入适量的DMF超声溶解,用DMF稀释至刻度,精密量取1 ml上述液体于10 ml容量瓶中,用DMF稀释至刻度。

    实验结果:色谱图良好,异丙醇对照品及市售产品均在6.84 min附近有峰且峰型良好,乙酸乙酯对照品及市售产品均在9.25 min附近有峰且峰型良好,乙酸丁酯对照品及市售产品均在14.07 min附近有峰且峰型良好;苯甲醇标准曲线、乙酸乙酯标准曲线和乙酸丁酯标准曲线的回归方程分别为:

    Y = 20152X + 2.692, r=1.000

    Y = 15311X + 33.45 ,r=0.999

    Y = 24428X – 17.33, r=0.999

    经计算得市售产品中异丙醇的使用量为35.1%,乙酸乙酯的使用量为21.4%,乙酸丁酯的使用量为5.3%。即三者使用比例为:6.6∶4∶1。

  • 采用硝化纤维(4%~8%)作为成膜材料,蓖麻油(1%~9%)为增塑剂,苯甲醇(4%)为抑菌剂,棕榈酸异丙酯(IPP,2%)为皮肤柔润剂,樟脑(0.3%)为芳香剂,以异丙醇、乙酸乙酯、乙酸丁酯(三者比例为6.6∶4∶1)作为溶剂制备创伤敷料。制备方法如下:于50 ml烧杯中精密称定处方量蓖麻油、苯甲醇、IPP、樟脑,加入上述3种混合溶剂使混合均匀,加入处方量硝化纤维,密封静置过夜待硝化纤维充分溶解,过夜后搅拌使硝化纤维混合均匀,超声除气泡即得。

  • 精密称定2 g按“2.2.1”项制备的液体创伤敷料,加入20 ml乙酸乙酯稀释使之混合均匀、黏度下降并充分溶解。将此液体置于90 mm培养皿中待溶剂挥干后可见均一透明无色薄膜。所制薄膜外观如图1所示。

  • 按照中华人民共和国医药行业标准YY/T 0471-2004对直接接触类创伤敷料,进行舒适性、防水性、透气性的考察。舒适性考察主要为考察敷料薄膜的抗张强度及断点伸长百分率[8-9];防水性考察薄膜的防水能力;透气性考察薄膜的水蒸气透过率(MVTR)[10]。抗张强度及断点伸长百分率的考察运用拉伸试验机,并采用公式1、公式2进行计算;防水性的考察采用倒杯法,记录24 h后的重量差异,如图2所示,以公式3进行计算;MVTR的考察方法:在西林瓶中加入蒸馏水,用薄膜覆盖密封,使水液面距薄膜(5±1)mm,置干燥器中,记录24 h后的重量差异,以公式4进行计算。

    式中,F为拉伸力;S为薄膜面积;Lmax为拉伸最大距离;L0为初始膜长;M0为初始西林瓶重量;M24h为24 h后西林瓶重量;MW为西林瓶内水重量;s为瓶口面积;t为时间24 h。

  • 分别采用4%、6%、8%的硝化纤维制备液体创伤敷料,对所制的薄膜进行评价,其断点伸长百分率、防水性能考察的水透过率及MVTR值随着硝化纤维用量的增加呈下降趋势,抗张强度随着硝化纤维用量的增加呈上升趋势。其考察结果如图3~图6所示:

    图3图4可知,硝化纤维的用量为4%、6%时,断点伸长百分率在170%以上,可认为薄膜韧性较好,在伤口表面有较好的舒适性,而硝化纤维用量为8%时,其断点伸长百分率较低,不足150%;在硝化纤维用量为4%时,所制薄膜过薄,导致其抗张强度较差,不及2.0 MPa。从图5可知,MVTR值在0.3~0.6 mg/(cm2·h)之间,随硝化纤维用量增加而减小,但均具有一定的透气性;由图6可知,三个不同梯度的硝化纤维在24 h内其水损失率均在2.5%以下,可认为防水性良好。综上考察结果,本次采用的硝化纤维用量为6%。

  • 确定硝化纤维使用量为6%后,分别采用1%、5%、9%用量的蓖麻油制备液体创伤敷料,对所制的薄膜进行评价,由图7图8可知,其断点伸长百分率随蓖麻油用量增加呈上升趋势,在蓖麻油使用量为1%时断点伸长百分率较差,不及150%,在5%~9%上升趋势明显且在蓖麻油用量为9%时达到190%,断点伸长百分率值数据较为理想;抗张强度随蓖麻油用量未呈明显下降趋势,反而是在蓖麻油使用量为5%时具有最大的抗张强度,而伸长率较好的9%用量蓖麻油处方抗张强度明显较小,在2.5 MPa左右,故蓖麻油用量选用浓度为5%。

    关于蓖麻油对防水性能和透气性能的影响如图9图10所示,蓖麻油用量为1%时其MVTR值明显高于5%和9%时,且其水损失率也高于5%和9%时,由于5%与9%的防水性没有太大的差异。由此可以得出的结论是,随着蓖麻油的加入,创伤敷料的透气性变差,同时其防水性能却有所增强,1%用量蓖麻油透气性能极佳,但机械性能及防水性相对较差,又因其水损失率24 h也没有达到5%,也可以认为其防水性能良好。所以下一步的考察尽量满足透气性的需求。

    综合断点伸长百分率、抗张强度、MVTR值、水损失率,在保证机械强度的同时尽量满足其透气性的要求。拟在1%~5%之间再另设梯度进行考察。拟定蓖麻油使用量为2%、3%、4%时对上述指标再行考察。

    图11图12可知处方断点伸长百分率及抗张强度在1%~5%范围内随蓖麻油用量的增加总体上均有一定的上升趋势。断点伸长百分率在蓖麻油用量为1%、2%时相差不大,在2%~5%时有明显的上升趋势;抗张强度在蓖麻油用量1%、2%时和4%、5%时相差不大,在蓖麻油用量从2%~4%时有明显的上升趋势。

    图13图14可知在蓖麻油用量为1%~5%范围内MVTR值及水损失率随处方中蓖麻油用量的增加而呈下降趋势。

    综合以上几个因素对处方中的蓖麻油用量进行考察,从所制薄膜的机械性能来看,在蓖麻油用量为1%~3%时,断点伸长百分率不及160%,抗张强度较差,不及3.60 MPa,故此用量不予考虑,从所制薄膜的防水透气效果来看,4%、5%用量均有一定的透气效果,且防水性测试结果显示二者水损失率均不超过2.50%。综上考虑,确定蓖麻油的使用量为4%。

  • 本文对市售产品的抑菌剂含量及溶剂组成进行了分析,以此作为基础对自制的液体创伤敷料进行单因素考察,确定了硝化纤维的最终用量为6%,蓖麻油的使用量为4%,所成薄膜具有良好的机械性能,具有透气性的同时又有着良好的防水效果。硝化纤维为主要的成膜材料,其用量对几个评价指标均有影响,其主要原因是其使用量的不同可造成所成薄膜的厚度不同,即创伤敷料薄膜厚度与硝化纤维用量成正比,其膜的厚度必然影响各项指标性能。蓖麻油作为增塑剂,对处方的影响主要在于:蓖麻油的加入能改变硝化纤维聚合物链之间的结构,使链与链之间的作用力产生变化从而在一定程度上影响薄膜的塑性。其次,蓖麻油的加入,可能堵塞了硝化纤维薄膜的纳米孔道,故呈现出其用量增加透气性能下降的趋势。

    皮肤创伤,在临床和日常生活中都较为常见,伤口愈合的速度一定程度上取决于创伤表面环境,创伤表面环境需保持一定的潮湿性,即湿润表面可以加速伤口愈合,因此良好的创伤敷料,应具有一定的透气性,对于日常伤口来说,由于伤口表面的复杂,使用在创伤表面的敷料也应具有一定的机械性能。本实验主要探讨了硝化纤维和蓖麻油的用量对创伤敷料性能的影响,为下一步制备性能更加优良的创伤敷料提供研究基础。